Previous page     Contents     Next page

3.3 g Phase transition and electronic structure: the high-pressure behaviour of the Ba-Cr analogue of gillespite (R. Miletich, R.J. Angel and J.R. Sowerby)

Gillespite, a barium-iron sheet silicate (BaFeSi4O10), was one of the first examples for which single-crystal X-ray diffraction in a diamond-anvil cell was used to investigate a pressure-induced structural phase transition. The tetragonal-to-orthorhombic transition, which occurs at relatively moderate pressures between 1.2 and 1.8 GPa, is known to be reversible and first-order in character. The relative size of the eight-fold coordinated Ba cation was thought to control the transition as the coordination number of Ba changes from 8 to 10. Moreover, the planar four-fold coordination of the Fe2+ transforms to a uniaxially elongated octahedron, which explains the characteristic colour change from red to blue observed for this pressure-induced transition. Even though both the low and the high-pressure polymorphs are structurally well characterized, the mechanism of the transition is poorly understood; symmetry analysis suggests that the transition could be a two-step process involving an intermediate phase.

In order to understand the mechanisms driving the transition on a microscopic scale, the gillespite-type analogue BaCrSi4O10 was chosen for high-pressure investigations, because it was found to approach gillespite closest from the point of view of atomic size (see also Annual Report 1995). High-pressure investigations by means of single-crystal X-ray diffraction and optical absorption spectroscopy were performed in diamond-anvil cells to quasihydrostatic pressures of ~10 and ~13 GPa. The optical absorption spectra to a maximum of 12.5 GPa are characterized by spin-allowed d-d transition bands as typical for square-planar coordinated Cr2+ cations. The changes within the spectra are continuous with band shifts of about 63 cm-1/GPa. The crystal field stabilisation energy rises from 13600 to 13850 cm-1 at maximum pressure whereas the t2g splitting (~3530 cm-1) remains virtually unchanged. For pressures in excess of 12.5 GPa we observe a color change from pink to blue thus indicating a transition from a square-planar to a distorted six-fold co-ordination. The observed phase change is irreversible and appears to be due to amorphization.

P-V data collected by single-crystal diffraction are suggestive of a change in the pressure-dependence of the unit-cell parameters between ~2 and ~3 GPa, although the lattice symmetry remains tetragonal at all pressures up to 10 GPa. The changes, which are indicative of a tetragonal-to-tetragonal phase transition, appear to be related to a P4/ncc-P4212 transition as indicated by preliminary refinements of the crystal structure at high pressures. The high-pressure polymorph, which appears to be an intermediate phase between the two gillespite polymorphs, retains the square-planar configuration around the Cr2+ atoms which explains why the absorption spectra are basically unaffected by the transition. The high-pressure investigations reveal that the structure of the Cr analogue of gillespite, although being so similar to gillespite itself, does not undergo the I-II transition reported for gillespite, at least not to a maximum pressure of 12.5 GPa. It appears that the different electronic d-configurations control the phase stability rather than the relative size of the Ba cations as previously suggested. Such a model appears to be very likely as the square-planar geometry is more favoured by the Cr2+ d4configuration than by the d6 configuration of Fe2+ in gillespite. The example demonstrates the major influence of the electronic structure of transition-metal cations in a silicate structure, which reveals a shift of the transition pressure in this example by at least 10 GPa, and has to be considered to be important even for other silicate systems at high pressures.

Bayerisches Geoinstitut, University of Bayreuth, 95440 Bayreuth, Germany
Tel: +49-(0) 921 55 3700 / 3766, Fax: +49-(0) 921 55 3769, E-mail: bayerisches.geoinstitut(at)uni-bayreuth.de